ASA

  • ASA IH801
ASA IH801

ASA IH801

  • Product description: ASA IH801
  • INQUIRY

Application: Automotive Part (Radiator Grill, Side Mirror)

Grade: Injection Molding


Properties

Test Condition

Test Method

Unit

Typical Value

Physical

Specific Gravity

ASTM D792

g/cm3

1.08

Molding Shrinkage (Flow), 3.2mm

ASTM D955

%

0.4-0.6

Melt Flow Rate

220°C/10kg

ASTM D1238

g/10min

6

Mechanical

Tensile Strength

23°C

ASTM D638

Mpa

50

Elongation at break

23°C

ASTM D638

%

15

Flexural Modulus

23°C

ASTM D790

Mpa

2200

Flexural Strength

23°C

ASTM D790

Mpa

65

Rockwell Hardness

R-Scale

ASTM D785

102

IZOD Impact Strength (Notched)

23°C 3.2mm

ASTM D256

J/M

180

IZOD Impact Strength (Unnotched)

23°C 3.2mm

ASTM D256

J/M

368

Thermal

Heat Deflection Temperature

1.82Mpa

ASTM D648

°C

96

Flammability

1.6mm

UL94

class

HB


Processing Guide (Injection Molding)

Processing Parameters

Unit

Value

Drying Temperature

°C

80 -95

Drying Time

hrs

3-5

Mold Temperature Range

ISO 294

°C

60

Melt Temperature

ISO 294

°C

240 ~ 280

Injection Velocity

ISO 294

mm/s

200

Note: Recommend initial lower temperatures settings to avoid material degradation/hang-up in die & purge material from extruder prior to shutdown.


Package&Storage

25kg or 1000kg PE-bag on pallet, shrink or wrapped with PE film.

In dry areas with normal temperature control, IH801 pellets can be stored for relatively long periods of time without any change in mechanical properties.

With unstable colors, however, storage over a number of years can give rise to some change in color. Under poor storage conditions, IH801 absorbs moisture, but this can be removed by drying.

PREVIOUS:ASA EL101 NEXT:CPVC Compound

CONTACT US

Contact: HAN

Phone: 86-15169610360

Tel: 0086-0536-8206760

Email: info@novistagroup.com

Add: Floor 17th , #2 Building CBD No.4778 Shengli East Street,WeiFang City,Shandong,P.R. of China.